很多種類的產品模具在制造加工的過程中拋光工作要做的非常的到位，這樣才能對模具的質量產生好的影響，那么模具的拋光會受哪些因素的影響呢？
Many kinds of product molds in the process of manufacturing and processing polishing work to do very in place, so as to have a good impact on the quality of the mold, so the polishing of the mold will be affected by what factors?
模具拋光不僅能滿足產品外觀光澤度的要求，同時還能改善產品的耐腐蝕性和耐磨性。所以模具拋光對產品是有實質性的好處的。
山東模具制造廠家認為如果熱處理不當，鋼材表面硬度不均或特性上有差異，會給拋光造成困難。
Die polishing can not only meet the requirements of gloss, but also improve the corrosion resistance and wear resistance of products. So die polishing is of substantial benefit to the product. Shandong mold manufacturers believe that if improper heat treatment, uneven hardness of steel surface or differences in characteristics, will cause difficulties to polishing.
優質的鋼材是獲得良好拋光質量的前提條件，鋼材中的各種夾雜物和氣孔都會影響拋光效果。要達到良好的拋光效果，工件必須在開始機械加工時要注明拋光的表面粗糙度，當一件工件確定需要鏡面拋光時，必須要選拋光性能好的鋼材并且都經過熱處理否則達不到預期的效果。
High quality steel is the prerequisite to obtain good polishing quality. Various inclusions and pores in steel will affect the polishing effect. In order to achieve good polishing effect, the workpiece must be marked at the beginning of the machining surface roughness, when a workpiece is determined to mirror polishing, must be selected with good polishing performance of steel and heat treatment or not to achieve the desired effect.
由于拋光主要是靠人工完成，所以人的技能目前還是影響拋光質量的主要原因。一般認為拋光技術影響表面粗糙度，其實好的拋光技術還要配合優質的鋼材以及正確的熱處理工藝，才能得到滿意的拋光效果；反之，拋光技術不好，就算鋼材再好也做不到鏡面效果。
Since polishing is mainly done manually, human skills are still the main reason for affecting the quality of polishing. It is generally believed that polishing technology affects surface roughness. In fact, good polishing technology should be matched with high quality steel and correct heat treatment process to obtain satisfactory polishing effect. On the contrary, the polishing technology is not good, even if the steel is good, it can not do the mirror effect.
材料在機械加工過程中，表層會因熱量、內應力或其他因素而損壞，切削參數不當會影響拋光效果。電火花加工后的表面比機械加工或熱處理后的表面更難研磨，因此電火花加工結束前應采用電火花精修整，否則表面會形成硬化薄層。
Material in the process of mechanical processing, the surface will be damaged by heat, internal stress or other factors, improper cutting parameters will affect the polishing effect. Edm surfaces are more difficult to grind than machined or heat treated surfaces, so edM finishing should be used at the end of edM, otherwise the surface will form a hardened thin layer.
The polishing of the mold will be affected by a number of factors related content is the above, if you have questions about this aspect might as well come to our www.zsxinyuanbuye.com.cn website to discuss.